PDF

HALLSTAR® DIOPLEX® VLV

Common Name: POLYESTER ADIPATE
Product Code: A373
Brand: Dioplex® HallStar®.

HALLSTAR DIOPLEX VLV is a highly efficient, very easy processing, very low viscosity polymeric plasticizer. It has similar handleability profile to standard monomerics yet provides an improvement in the level of resistance to extraction by various media when compared to monomerics such as DOP, DINP and linear phthalates.

In addition, HALLSTAR DIOPLEX VLV offers excellent cold flex properties and compares favorably with most phthalates and trimellitates.

With a benign environmental / legislative profile, low viscosity is an essential ingredient in plastisol formulations as a non-phthalate.

HALLSTAR DIOPLEX VLV IS AVAILABLE GLOBALLY.

Viscosity at 25°C, cSt	<100
Specific Gravity, 20°C	1.0
Hydroxyl Value, mg KOH/g	40
Acid Value, mg KOH / g	2.5
Appearance	Straw-colored
Color Hazen (PT/Cobalt)	250
Packaging	5 gallon pail - 25kgs Tote - 1000kgs Drum - 200kgs 5 gallon pail - 25kgs Tote - 1000kgs Drum - 200kgs

PVC-EU

100% Modulus, MN/m2	5.0
100% Modulus, MN/m2	5.0
Tensile Strength, MN/m2	14.3
Tensile Strength, MN/m2	14.3
Elongation at Break, %	495
Elongation at Break, %	495
Shore A Hardness	63
Shore A Hardness	63
Tg, °C	-32
Tg, °C	-32
Low Temperature Brittle Point, °C	-44
Low Temperature Brittle Point, °C	-44
Low Temp Gehman T10,000 PSI, °C	-36
Low Temp Gehman T10,000 PSI, °C	-36
Volatilization	-13.3
Volatilization	-13.3
Immersion/Extraction, Weight change, %
Immersion/Extraction, Weight change, %
Mineral Oil	-16.6
Mineral Oil	-16.6
Olive Oil	-17.1
Olive Oil	-17.1
Hexane	-22.7
Hexane	-22.7
Distilled water	-1.1
Distilled water	-1.1
1% Soap Solution	-9.2
1% Soap Solution	-9.2

PVC-US

Shore A Hardness	63
Shore A Hardness	63
Elongation at Break, %	495
Elongation at Break, %	495
Tensile Strength, MPa	14.3
Tensile Strength, MPa	14.3
Tensile Strength, psi	2075
Tensile Strength, psi	2075
Tg, °C	-32
Tg, °C	-32
Low Temperature Brittle Point, °C	-44
Low Temperature Brittle Point, °C	-44
Low Temp Gehman T10,000 PSI, °C	-36
Low Temp Gehman T10,000 PSI, °C	-36
Volatilization	-13
Volatilization	-13
Immersion/Extraction, Weight change, %
Immersion/Extraction, Weight change, %
Hexane	-24
Hexane	-24
1% Soap Solution	-8.4
1% Soap Solution	-8.4
Cottonseed Oil	-17
Cottonseed Oil	-17
Distilled water	-1.4
Distilled water	-1.4
High humidity	-1.0
High humidity	-1.0
ABS	Good
ABS	Good
Polystyrene	Poor
Polystyrene	Poor

Global Compliance:

China
EU
USA

Polymers:

Acrylic resins
Nitrile
Nitrocellulose
Polymethyl methacrylate
Polyvinyl chloride
Vinyl chloride acetate
Acrylic resins
Nitrile
Nitrocellulose
Polymethyl methacrylate
Polyvinyl chloride
Vinyl chloride acetate

Applications:

Automotive sealant
Coated fabrics
Film and sheeting for use in low temperatures
Gaskets
General-purpose film
Low viscosity plastisols
Phthalate alternative
Pigment dispersant
Plastisol coatings
PVC Film
Automotive sealant
Coated fabrics
Film and sheeting for use in low temperatures
Gaskets
General-purpose film
Low viscosity plastisols
Phthalate alternative
Pigment dispersant
Plastisol coatings
PVC Film

The information presented herein is believed to be accurate and reliable, but no warranty or guarantee, expressed or implied, is made regarding the information or the performance of any product. Further, nothing contained herein shall be taken as any inducement or recommendation to use, manufacture or sell that may infringe any patents or any other proprietary rights now or hereafter in existence, nor to imply compliance with any regulatory requirements